Exolit OP1312 1314 flame retardant PA6/66 nylon6/66

Exolit OP1312 1314 flame retardant PA6/66 nylon6/66

Payment Type: L/C,T/T,D/P
Incoterm: FOB,CFR,CIF
Min. Order: 40 Bag/Bags
Delivery Time: 7 Days

Basic Info

    Model No.: PN2131C/CD

    Appearance: Powder

    Color: White

Additional Info

    Packaging: 25kg/bag

    Productivity: 3,000 MT

    Brand: NOVISTA

    Transportation: Ocean,Land,Air

    Place of Origin: CHINA

    Supply Ability: 3,000 MT

    Certificate: ROHS/SGS

    HS Code: 3824999990

    Port: Qingdao

Product Description

ProFlame-PN2131C/CD is formulated Flame Retardant based on organic phosphorus component. It is suited for both GF-reinforced and unreinforced PA6/PA66 system. The polyamide compounds exhibit very good physical and electrical properties with PN2131C.

Technical Data: Items Spec

Appearance White free-flowing powder

P (as P2O5) content, % 18-21

1% TGA Temperature, °C ≥320

Average particle size, um D50≤15

PH value 4.5-6.5

Moisture,% ≤0.5

Solubility in water %,
25°C , g/100mL H2O ≤0.5

Whiteness ≥97

Recommended dosage:

Polymer

PA6

PA66

UL-94

GWFI

Unreinforced

17-20

15-18

V0(1.6mm)

960°C

20-30%GF-Reinforced

14-17

12-16

V0(1.6mm)

960°C

Processing instruction:

1. Pre-drying the polyamide,the moisture content should be below 0.1 % (by wt.).

2. The optimum conditions for incorporating should be determined in each individual case. Care must be taken to ensure homogeneous dispersion of all components.

3. The temperature of the polymer melt should not exceed 320 °C.

4. It is most suitable for equipment with weak shear force.

5. The processing temperature of Parallel twin-screw extruder should keep between 240 ~ 260 ℃ with

vacuum at the same time.The temperature is too high, the physical property loss of PA66 is large, and the yellowing is also large.

6. Do not use low-alkali or high-alkali fiberglass. High-quality non-alkali fiberglass is preferred.

Package & Storage:

Net weight 25KG Kraft bag with PE liner.

It is not dangerous cargo .You should handle the material according to the instruction described on SDS.


Typical Application Data 1-1

Material

Formula 1

Formula 2

Formula 3

Formula 4

PA6

82

-

-

-

30%GF/PA6

-

84

-

-

PA66

-

-

82

-

30%GF/PA66

-

-

-

85

PN2131C

18

16

17

15

Properties 1-2

Item

Testing Method

Formula 1

Formula 2

Formula 3

Formula 4

UL94 (1.6mm)

UL94-2013

V-0

V-0

V-0

V-0

GWIT

IEC 60695-2-13

800°C

830°C

810°C

850°C

GWFI

IEC 60695-2-12

960°C

960°C

960°C

960°C

CTI

IEC60112

550 V

600 V

560 V

600 V

Tensile Strength

GB/T 1040.1-2006

64 Mpa

95 Mpa

78 Mpa

120 Mpa

Flexural Strength

GB/T 9341-88

85 Mpa

145 Mpa

125 Mpa

180 Mpa

Flexural modulus

GB/T 9341-88

2700 Mpa

5012 Mpa

4012 Mpa

7500 Mpa

Notch impact strength

GB/T 9342-88

13 KJ/m2

10 KJ/m2

11 KJ/m2

6.5 KJ/m2

Looking for ideal Exolit OP1312 Manufacturer & supplier ? We have a wide selection at great prices to help you get creative. All the Exolit OP1314 are quality guaranteed. We are China Origin Factory of Flame Retardant Nylon6/66. If you have any question, please feel free to contact us.

Product Categories : Flame Retardant > Halogen-Free Flame Retardant

Send Inquiry

Tel:86-536-8206760

Fax:86-536-8206750

Mobile Phone:+8615336365800

Email:manager.han@novistagroup.com

Address:RM1232-1233,#4 Building No.4778 Shengli East Street, Weifang, Shandong